Leadpad
Leadpad is an uncured, non-silicone rubber pressure-equalizing sheets. The rubber pressure caul sheets is placed on the surface of the resin-base composite layer before the resin is cured in the molding process of the composite material,and is mainly used for transferring and distributing the pressure, so that the composite material is none of wrinkles, voids, delamination, deformation, bridging and so on, and can be used for blocking the overflow of the resin, and the use of the pressure-equalizing plate can greatly improve the quality of the product of the composite material, and at the same time effectively reduce the rework rate of the composite material component.
Leadpad-H
Leadpad-H and Leadpad-S are rubber pressure caul sheets specially designed for autoclave processing. Apply full vacuum throughout cure cycle and pressurize autoclave to 100 psi (7 bar), minimum recommended pressure is 45 psi (3 bar).Heat to 399°F (180°C) and hold for 2 hours, then cool to room temperature before removing vacuum and demolding from master mold.
Leadpad-H
|
Specifications |
|||
|
Colour |
Black |
||
|
Thickness/ in |
0.063 (1.6 mm) |
||
|
Width / in |
39.37 (1000 mm) |
||
|
Maximum Use Temperature/ ℉ |
401(205℃) |
||
|
Specific gravity / (g/cm3) |
1.19-1.20 |
||
|
Shelf life/month(packaging at23℃) |
12 |
||
|
Physical property |
|||
|
Elongation at break/% |
ASTM D412 |
400-430 |
|
|
Tensile strength/Mpa |
ASTM D412 |
≥8.2 |
|
|
Hardness of Shore A |
ASTM D2240 |
70 |
|
|
Shrinkage/% |
GJB 5873-20006 |
≤0.5% |
|
Leadpad-S
|
Specifications |
|||
|
Colour |
Black |
||
|
Thickness/ in |
0.079 (2.0 mm) |
||
|
Width / in |
37.40(950 mm) |
||
|
Maximum Use Temperature/ ℉ |
401(205℃) |
||
|
Specific gravity / (g/cm3) |
1.18-1.20 |
||
|
Shelf life/month(packaging at23℃) |
12 |
||
|
Physical property |
|||
|
Elongation at break/% |
ASTM D412 |
400-430 |
|
|
Tensile strength/Mpa |
ASTM D412 |
≥8.2 |
|
|
Hardness of Shore A |
ASTM D2240 |
70 |
|
|
Shrinkage/% |
GJB 5873-20006 |
≤0.5% |
|
Spiral wrap SW10-8
|
Specifications |
|
|
Use Temperature |
180℉(80℃) |
|
Material |
Polyethylene |
|
Solid State |
100% |
|
Colour |
White or Transparency |
|
Type |
3/8"OD - 3/10" ID (10mm OD - 8mm ID) |
WF125
|
Specifications |
|
|
Colour |
White |
|
Thickness /in |
0.15（3.8mm） |
|
Width/in |
60（1520mm） |
|
Weight/[g/m2] |
125 |
|
Maximum Use Temperature/οF |
400（205℃） |
|
Physical Properties |
||
|
Air permeability/[mm/s] |
GB/T 5453 |
≥2200 |
R85PA66
|
Specifications
|
|
|
Material
|
Nylon 66
|
|
Color
|
White with red tracer yarn
|
|
Width/in
|
4-70（100-1800mm）
|
|
Weight[g/㎡]
|
85
|
|
Maximum Use Temperature/οF
|
360（180℃）
|
|
Release agent
|
No
|
|
Physical Properties
|
||
|
Tensile Strength（MD）[N/2.0in]
|
GB/T 3923.1
|
≥1200
|
|
Tensile Strength（TD）[N/2.0in]
|
≥1000
|
|
LG150
|
Specifications
|
|
|
Colour
|
Black
|
|
Thickness/ in
|
0.12 (3 mm)
|
|
Width / in
|
0.47 (12 mm)
|
|
Maximum Use Temperature/ ℉
|
300 (150 ℃)
|
|
Physical property
|
||
|
Penetration / in
|
GB/T 4509
|
0.22-0.30 (5.5-7.5 mm)
|