Shanghai Leadgo-tech Co., Ltd

HOME > Products > Thermosetting composite

Thermosetting composite

The epoxy resin based carbon fiber reinforced prepreg developed by Shanghai Leadgo-tech Co., Ltd. can be applied to high impact composite components such as aerospace, wind power, etc. LMP series prepreg is a medium temperature curing system, which can be cured at 80 ℃ - 130 ℃. The recommended curing temperature and pressure are 80 ℃/30min+120 ℃/0.6MPa/120min.

LMP-33%-T700-12K-U-125gsm-600

LMP-33% - T700-12K-U-125gsm-600 is a medium temperature epoxy resin based carbon fiber reinforced unidirectional prepreg, the resin matrix is an epoxy resin developed by Shanghai Leadgo-tech Co., Ltd., and the reinforcement material is SYT49S-12K.

Project	Performance
Width/[mm]	600±10
Weight/[g/m²]	187±9
Resin content[%]	33±2
Fiber weight/[g/m²]	125±6
Volatiles[%]	≤0.5

Property	Unit	Parameter	Method
0° tensile strength of composite laminate	MPa	≥1420	ASTMD3039
90° tensile strength of composite laminate	MPa	≥35	ASTMD3039
0° flexural strength of composite laminate	MPa	≥1440	ASTM D790
0° flexural modulus of composite laminate	GPa	≥124	ASTM D790
90° flexural strength of composite laminate	MPa	≥70	ASTM D790
90° flexural modulus of composite laminate	GPa	≥7.5	ASTM D790

Tips: The thickness of carbon fiber composite plate is 2mm. The direction along the carbon fiber orientation corresponds to 0 °, and the direction perpendicular to the carbon fiber orientation corresponds to 90 °.

Tips: The thickness of carbon fiber composite plate is 2mm. The direction along the carbon fiber orientation corresponds to 0 °, and the direction perpendicular to the carb

LMP-38%-EGLASS-P-100gsm-600

LMP-38%-EGLASS-P-100gsm-600 is a medium temperature epoxy resin based Plain glass fabric reinforced prepreg, the resin matrix is an epoxy resin developed by Shanghai Leadgo-tech Co., Ltd., and the reinforcement material is 2116 E-glass fabric.

Project	Performance
Width/[mm]	600±10
Weight/[g/m²]	161±8
Resin content[%]	33±2
Fiber weight/[g/m²]	100±5
Volatiles[%]	≤0.5

LMP-42%-T300-3K-T-199gsm-600

LMP-42%-T300-3K-T-199gsm-600 is a medium temperature epoxy resin based carbon twill fabric reinforced prepreg, the resin matrix is an epoxy resin developed by Shanghai Leadgo-tech Co., Ltd., and the reinforcement material is T300-3K-2/2。

Project	Performance
Width/[mm]	600±10
Weight/[g/m²]	343±17
Resin content[%]	42±2
Fiber weight/[g/m²]	198±8
Volatiles[%]	≤0.5

Property	Unit	Parameter	Method
0° tensile strength of composite laminate	MPa	≥750	ASTMD3039
90° tensile strength of composite laminate	MPa	≥750	ASTMD3039
0° flexural strength of composite laminate	MPa	≥782	ASTM D790
0° flexural modulus of composite laminate	GPa	≥47	ASTM D790
90° flexural strength of composite laminate	MPa	≥782	ASTM D790
90° flexural modulus of composite laminate	GPa	≥47	ASTM D790

Tips: The thickness of carbon fiber composite plate is 2mm. The orientation along the carbon fiber fabric corresponds to the 0 ° direction, and the orientation perpendicular to the carbon fiber fabric corresponds to the 90 ° direction.

Total: 3 Pages 1/1