RMK vacuum kit
RMK is a vacuum kit which is composed of vacuum bagging film, infusion mesh and membrane fabric.The vacuum bagging film and membrane fabric are combined to form a confined space. The infusion mesh is placed in the middle to ensure the flow of air. The membrane fabric can function to achieve air permeability. It is widely used in the production of wind turbine blades and vacuum injection moldings
|
Specifications |
|
|
Thickness/in |
Resin impregnated fabric |
|
Width/in |
5.91(150mm)/7.87(200mm)/ 9.84(250mm)/11.81(300mm)/ 13.78(350mm)/ |
|
Length/in |
Customized according to requirements |
|
Maximum service temperature/°F |
300(150℃) |
LGVM360 membrane fabric
LGVM360 membrane fabric is a nylon release fabric with polyurethane coating on the back, which is widely used in resin flow diversion process. It is cleaned and heat-shaped, and processed with a single-sided polyurethane coating to achieve permeability and resin impermeability during use.
|
Parameter |
||
|
Specification |
120g/m2 |
150g/ m2 |
|
Colour |
Blue |
white |
|
Width/mm |
100-1500 |
100-1500 |
|
Areal density/[g/m2] |
115±10 |
150±15 |
|
Thickness/μm |
180±15 |
200±24 |
|
Ventilatory capacity/[mm/s] |
≥1.5 |
|
|
mold release |
NO |
|
|
Carrier material |
Nylon 6 |
|
|
Membrane material |
Polymeric Foam |
|
|
Membrane type |
Semi permeable |
|
|
Maximum use temperature/℃ |
120 |
|
LMP-33%-T700-12K-U-125gsm-600
|
Project
|
Performance
|
|
Width/[mm]
|
600±10
|
|
Weight/[g/m2]
|
187±9
|
|
Resin content[%]
|
33±2
|
|
Fiber weight/[g/m2]
|
125±6
|
|
Volatiles[%]
|
≤0.5
|
|
Property
|
Unit
|
Parameter
|
Method
|
|
0° tensile strength of composite laminate
|
MPa
|
≥1420
|
ASTMD3039
|
|
90° tensile strength of composite laminate
|
MPa
|
≥35
|
ASTMD3039
|
|
0° flexural strength of composite laminate
|
MPa
|
≥1440
|
ASTM D790
|
|
0° flexural modulus of composite laminate
|
GPa
|
≥124
|
ASTM D790
|
|
90° flexural strength of composite laminate
|
MPa
|
≥70
|
ASTM D790
|
|
90° flexural modulus of composite laminate
|
GPa
|
≥7.5
|
ASTM D790
|
Tips: The thickness of carbon fiber composite plate is 2mm. The direction along the carbon fiber orientation corresponds to 0 °, and the direction perpendicular to the carbon fiber orientation corresponds to 90 °.
LMP-38%-EGLASS-P-100gsm-600
LMP-38%-EGLASS-P-100gsm-600 is a medium temperature epoxy resin based Plain glass fabric reinforced prepreg, the resin matrix is an epoxy resin developed by Shanghai Leadgo-tech Co., Ltd., and the reinforcement material is 2116 E-glass fabric.
|
Project |
Performance |
|
Width/[mm] |
600±10 |
|
Weight/[g/m2] |
161±8 |
|
Resin content[%] |
33±2 |
|
Fiber weight/[g/m2] |
100±5 |
|
Volatiles[%] |
≤0.5 |
LMP-42%-T300-3K-T-199gsm-600
LMP-42%-T300-3K-T-199gsm-600 is a medium temperature epoxy resin based carbon twill fabric reinforced prepreg, the resin matrix is an epoxy resin developed by Shanghai Leadgo-tech Co., Ltd., and the reinforcement material is T300-3K-2/2。
|
Project |
Performance |
|
Width/[mm] |
600±10 |
|
Weight/[g/m2] |
343±17 |
|
Resin content[%] |
42±2 |
|
Fiber weight/[g/m2] |
198±8 |
|
Volatiles[%] |
≤0.5 |
|
Property |
Unit |
Parameter |
Method |
|
0° tensile strength of composite laminate |
MPa |
≥750 |
ASTMD3039 |
|
90° tensile strength of composite laminate |
MPa |
≥750 |
ASTMD3039 |
|
0° flexural strength of composite laminate |
MPa |
≥782 |
ASTM D790 |
|
0° flexural modulus of composite laminate |
GPa |
≥47 |
ASTM D790 |
|
90° flexural strength of composite laminate |
MPa |
≥782 |
ASTM D790 |
|
90° flexural modulus of composite laminate |
GPa |
≥47 |
ASTM D790 |
Tips: The thickness of carbon fiber composite plate is 2mm. The orientation along the carbon fiber fabric corresponds to the 0 ° direction, and the orientation perpendicular to the carbon fiber fabric corresponds to the 90 ° direction.