Wet Peel Ply
Wet Peel Ply is a kind of stripable cloth impregnated with 120℃ epoxy resin. The stripable cloth is pasted on the surface of the preformed body of the composite material before curing and is ripped off after curing. The roughness and bonding strength of the fabric can be improved by leaving the fabric texture of the stripable fabric on the surface of the composite material. Wet Peel Ply suitable for the vacuum bag pressing process of autoclave. The recommended curing process is 120℃ for 2h.
Parameter |
|
Product description |
Resin impregnated fabric |
Colour |
black/transparent |
Resin content / [%] |
48 |
Areal density / [g/m2] |
163 |
Specification / [m] |
W:1.0 L:50 |
LTP21-CF unidirectional tape
Type |
Density g/cm3 |
Fiber content %wt |
Thickness mm |
Area weight g/m2 |
Method |
GB/T1033 |
GB/T9345.1 |
GB/T 6672 |
GB/T 20220 |
LTP21-CF-45%-330GSM |
1.11 |
45 |
0.29 |
330 |
LTP21-CF-50%-300GSM |
1.19 |
50 |
0.26 |
300 |
Property |
Unit |
LTP21-CF-45%-330GSM |
LTP21-CF-50%-300GSM |
Method |
0 ° tensile strength of unidirectional tape |
MPa |
≥750 |
≥900 |
ASTMD3039 |
0 ° tensile strength of composite plate |
MPa |
≥400 |
≥450 |
ASTMD3039 |
90 ° tensile strength of composite plate |
MPa |
≥400 |
≥450 |
ASTMD3039 |
0° flexural strength of composite plate |
MPa |
≥120 |
≥140 |
ASTM D790 |
0 ° flexural modulus of composite plate |
GPa |
≥28 |
≥36 |
ASTM D790 |
90 ° flexural strength of composite plate |
MPa |
≥85 |
≥110 |
ASTM D790 |
90 ° flexural modulus of composite plate |
GPa |
≥19 |
≥22 |
ASTM D790 |
Note: the composite plate is made of 0°/90° symmetrical layer; the data in the table are the average values in the laboratory, which are only for reference in use.
LTP21-GF unidirectional tape
Type |
Density g/cm3 |
Fiber content %wt |
Thickness mm |
Area weight g/m2 |
Method |
GB/T1033 |
GB/T9345.1 |
GB/T 6672 |
GB/T 20220 |
LTP21-GF-60%-485GSM |
1.49 |
60 |
0.32 |
485 |
LTP21-GF-65%-450GSM |
1.53 |
65 |
0.29 |
450 |
LTP21-GF-70%-415GSM |
1.64 |
70 |
0.26 |
415 |
Property |
Unit |
LTP21-GF-60% -485GSM |
LTP21-GF-65% -450GSM |
LTP21-GF-70% -415GSM |
Method |
0 ° tensile strength of unidirectional tape |
MPa |
≥700 |
≥750 |
≥800 |
ASTMD3039 |
0 ° tensile strength of unidirectional tape |
MPa |
≥300 |
≥320 |
≥340 |
ASTMD3039 |
0 ° tensile strength of composite plate |
MPa |
≥300 |
≥320 |
≥340 |
ASTMD3039 |
90 ° tensile strength of composite plate |
MPa |
≥300 |
≥320 |
≥340 |
ASTM D790 |
0° flexural strength of composite plate |
GPa |
≥15.5 |
≥18.5 |
≥20 |
ASTM D790 |
0 ° flexural modulus of composite plate |
MPa |
≥230 |
≥250 |
≥275 |
ASTM D790 |
90 ° flexural strength of composite plate |
GPa |
≥8 |
≥10 |
≥11 |
ASTM D790 |
Note: the composite plate is made of 0°/90° symmetrical layer; the data in the table are the average values in the laboratory, which are only for reference in use.
LRF160
Specifications
|
|
Colour
|
Red
|
Thickness/in
|
0.002" (45um)
|
Width/in
|
59" (1.5m)
|
Weight/[g/m2]
|
40
|
Maximum Use Temperature/℉
|
300(150℃)
|
Tensile Strengt(MD)/MPa
|
ASTM D882
|
≥40
|
Tensile Strengt(TD)/MPa
|
≥25
|
|
Elongation(MD)/%
|
ASTM D882
|
≥400
|
Elongation(TD)/%
|
≥400
|
*All properties are tested under the condition of no hole.