Shanghai Leadgo-tech Co., Ltd

LMP-33%-T700-12K-U-125gsm-600

LMP-33% - T700-12K-U-125gsm-600 is a medium temperature epoxy resin based carbon fiber reinforced unidirectional prepreg, the resin matrix is an epoxy resin developed by Shanghai Leadgo-tech Co., Ltd., and the reinforcement material is SYT49S-12K.

Project	Performance
Width/[mm]	600±10
Weight/[g/m²]	187±9
Resin content[%]	33±2
Fiber weight/[g/m²]	125±6
Volatiles[%]	≤0.5

Property	Unit	Parameter	Method
0° tensile strength of composite laminate	MPa	≥1420	ASTMD3039
90° tensile strength of composite laminate	MPa	≥35	ASTMD3039
0° flexural strength of composite laminate	MPa	≥1440	ASTM D790
0° flexural modulus of composite laminate	GPa	≥124	ASTM D790
90° flexural strength of composite laminate	MPa	≥70	ASTM D790
90° flexural modulus of composite laminate	GPa	≥7.5	ASTM D790

Tips: The thickness of carbon fiber composite plate is 2mm. The direction along the carbon fiber orientation corresponds to 0 °, and the direction perpendicular to the carbon fiber orientation corresponds to 90 °.

Tips: The thickness of carbon fiber composite plate is 2mm. The direction along the carbon fiber orientation corresponds to 0 °, and the direction perpendicular to the carb

LMP-38%-EGLASS-P-100gsm-600

LMP-38%-EGLASS-P-100gsm-600 is a medium temperature epoxy resin based Plain glass fabric reinforced prepreg, the resin matrix is an epoxy resin developed by Shanghai Leadgo-tech Co., Ltd., and the reinforcement material is 2116 E-glass fabric.

Project	Performance
Width/[mm]	600±10
Weight/[g/m²]	161±8
Resin content[%]	33±2
Fiber weight/[g/m²]	100±5
Volatiles[%]	≤0.5

LMP-42%-T300-3K-T-199gsm-600

LMP-42%-T300-3K-T-199gsm-600 is a medium temperature epoxy resin based carbon twill fabric reinforced prepreg, the resin matrix is an epoxy resin developed by Shanghai Leadgo-tech Co., Ltd., and the reinforcement material is T300-3K-2/2。

Project	Performance
Width/[mm]	600±10
Weight/[g/m²]	343±17
Resin content[%]	42±2
Fiber weight/[g/m²]	198±8
Volatiles[%]	≤0.5

Property	Unit	Parameter	Method
0° tensile strength of composite laminate	MPa	≥750	ASTMD3039
90° tensile strength of composite laminate	MPa	≥750	ASTMD3039
0° flexural strength of composite laminate	MPa	≥782	ASTM D790
0° flexural modulus of composite laminate	GPa	≥47	ASTM D790
90° flexural strength of composite laminate	MPa	≥782	ASTM D790
90° flexural modulus of composite laminate	GPa	≥47	ASTM D790

Tips: The thickness of carbon fiber composite plate is 2mm. The orientation along the carbon fiber fabric corresponds to the 0 ° direction, and the orientation perpendicular to the carbon fiber fabric corresponds to the 90 ° direction.

LTP21-CF unidirectional tape

Type	Density g/cm³	Fiber content %wt	Thickness mm	Area weight g/m²
Method	GB/T1033	GB/T9345.1	GB/T 6672	GB/T 20220
LTP21-CF-45%-330GSM	1.11	45	0.29	330
LTP21-CF-50%-300GSM	1.19	50	0.26	300

Property	Unit	LTP21-CF-45%-330GSM	LTP21-CF-50%-300GSM	Method
0 ° tensile strength of unidirectional tape	MPa	≥750	≥900	ASTMD3039
0 ° tensile strength of composite plate	MPa	≥400	≥450	ASTMD3039
90 ° tensile strength of composite plate	MPa	≥400	≥450	ASTMD3039
0° flexural strength of composite plate	MPa	≥120	≥140	ASTM D790
0 ° flexural modulus of composite plate	GPa	≥28	≥36	ASTM D790
90 ° flexural strength of composite plate	MPa	≥85	≥110	ASTM D790
90 ° flexural modulus of composite plate	GPa	≥19	≥22	ASTM D790

Note: the composite plate is made of 0°/90° symmetrical layer; the data in the table are the average values in the laboratory, which are only for reference in use.

LTP21-GF unidirectional tape

Type	Density g/cm³	Fiber content %wt	Thickness mm	Area weight g/m²
Method	GB/T1033	GB/T9345.1	GB/T 6672	GB/T 20220
LTP21-GF-60%-485GSM	1.49	60	0.32	485
LTP21-GF-65%-450GSM	1.53	65	0.29	450
LTP21-GF-70%-415GSM	1.64	70	0.26	415

Property	Unit	LTP21-GF-60% -485GSM	LTP21-GF-65% -450GSM	LTP21-GF-70% -415GSM	Method
0 ° tensile strength of unidirectional tape	MPa	≥700	≥750	≥800	ASTMD3039
0 ° tensile strength of unidirectional tape	MPa	≥300	≥320	≥340	ASTMD3039
0 ° tensile strength of composite plate	MPa	≥300	≥320	≥340	ASTMD3039
90 ° tensile strength of composite plate	MPa	≥300	≥320	≥340	ASTM D790
0° flexural strength of composite plate	GPa	≥15.5	≥18.5	≥20	ASTM D790
0 ° flexural modulus of composite plate	MPa	≥230	≥250	≥275	ASTM D790
90 ° flexural strength of composite plate	GPa	≥8	≥10	≥11	ASTM D790